Microwave-Induced Hydrogen Plasma as a New Synthesis Process for High-Entropy Carbides.

Microwave-Induced Hydrogen Plasma (MIHP) is introduced as a novel synthesis route for producing high-entropy carbides (HECs), offering an alternative to conventional mechanical alloying and/or sintering techniques. In this study, a representative HEC composition, MoNbTaVWC5, was successfully synthesized using MIHP processing at 200 Torr. The process employs microwave energy to generate hydrogen plasma to facilitate carbothermal reduction of metal oxide precursors. The plasma environment generates abundant reactive atomic hydrogen species, which enhance reaction spontaneity and promote efficient HEC formation. X-ray diffraction confirmed the formation of a single-phase rocksalt-type face-centered cubic structure. Scanning electron microscopy combined with energy-dispersive X-ray spectroscopy confirmed uniform elemental distribution within the synthesized microstructure. Nanoindentation measurements yielded hardness and elastic modulus values consistent with literature reports for similar compositions. X-ray photoelectron spectroscopy confirmed the chemical state of carbon to be primarily bonded with metals as carbides, with only minor oxygen present as metal-oxides. Raman spectroscopy performed over the 750-1900 cm-1 range yielded a featureless spectrum with no detectable D or G bands often observed for sp2-hybridized disordered carbon, graphite, or graphene materials. These results validate the structural and chemical purity of the synthesized HECs. This work aims to demonstrate the feasibility and reproducibility of MIHP as a synthesis method for HECs.