Numerical Simulation and Optimization of Furnace Roll Casting Production Technology.

This study investigates the use of steel and cast iron for producing cast furnace rolls to replace welded rolls, which often fail from cracks and limited durability. Casting had not been previously considered by the manufacturer, but rising demands for durability and quality make it a promising alternative. Material selection focused on mechanical properties, wear resistance, and production costs. To ensure casting quality, Magmasoft 6.0 software was applied for detailed simulation of casting, solidification, and cooling. Results showed that steel alloys (GS-34CrMo4 and GS-20Mn5) are prone to shrinkage and porosity, which cannot be fully avoided even with feeders. In contrast, GJS-500-7 cast iron exhibited low shrinkage tendency and minimal defects, proving suitable for production while reducing costs. It also offers lower weight and efficient metal use, improving cost-effectiveness. Detected defects were concentrated in the central casting area, where they have little impact on functionality. Based on sixteen simulations, GJS-500-7 cast iron emerged as the most suitable material for furnace rolls thanks to its thermal resistance, castability, low porosity, and ability to meet required specifications. This process optimization represents an efficient, cost-effective choice, improving final product quality and creating new opportunities for the manufacturer.