Utilization of Brick Powder in Blended Cement Compositions: Rheological, Mechanical, and Microstructural Properties.

The growing demand for eco-efficient construction materials has driven the development of low-clinker cement systems incorporating recycled mineral additives. Finely ground brick powder represents one of such materials with high pozzolanic potential. This article presents an experimental study on the effect of partially replacing slag cement CEM III and ordinary rapid-hardening cement CEM I with brick powder waste of different chemical compositions and fineness levels (63, 32, and 15 µm) on the physical and mechanical properties of blended cement mortars. Compressive and flexural strengths were determined at 2, 7, and 28 days, along with the strength activity index (SAI). Additionally, the setting times and standard consistency were investigated, with the latter showing a correlation with the workability of fresh mortars. Comprehensive microstructural analysis (TGA, SEM, EDX) confirmed the pozzolanic activity of the brick powder, which was manifested by the formation of C-S-H and C-A-S-H phases. The highest strength characteristics were achieved with a 15% replacement of cement by brick powder with a fineness of 32 μm and an increased SiO2 content (63.06%). Comparative analysis with fly ash- and silica fume-modified mortars revealed that brick powder exhibits comparable performance, confirming its suitability as an active mineral additive.