Leakage-Proof and High-Conductivity Composite Phase Change Material Using Low-Melting-Point-Alloy-Encapsulated Copper Foam/Paraffin for Superior Thermal Homogeneity in Lithium-Ion Battery Modules.

Ensuring thermal stability is a major concern in lithium-ion battery systems. Although phase change materials (PCMs) provide a passive approach for temperature regulation, they are limited by poor heat conduction and potential leakage during phase transitions. This study develops a novel composite PCM (CPCM) using paraffin (PA) as the matrix, copper foam (CF) as a conductive skeleton (10-30 pores per inch, PPI), and a low-melting-point alloy (LMA) as an encapsulant to prevent leakage. The effects of CF pore size on thermal conductivity, impregnation ratio, and leakage resistance were systematically investigated. Results show that CPCM with 10 PPI CF achieved the highest thermal conductivity (4.42 W·m-1·K-1), while LMA encapsulation effectively eliminated leakage. The thermal management performance was evaluated on both a single 18,650 LIB cell and a 2S2P module during rate discharging at 1C, 2C, and 3C. For the module at 3C, the 10 PPI CPCM significantly lowered the maximum temperature from 75.9 °C to 44.6 °C and critically reduced the maximum temperature difference between cells from 10.2 °C to a safe level of 1.2 °C, significantly improving temperature uniformity. This work provides a high-conductivity and leakage-proof CPCM solution based on LMA-encapsulated CF/PA for enhanced thermal safety and uniformity in LIB modules.