Quasi-Static and High Strain-Rate Behavior of Carbon Fiber Reinforced Modified BOFS Concrete.

This study examines the mechanical properties of concrete in which natural aggregates are entirely replaced by modified basic oxygen furnace slag (MBOFS) and reinforced with chopped carbon fibers, under both dynamic and quasi-static loading conditions. The carbon fiber (CF) was subjected to heat treatment and pneumatic dispersion prior to mixing, and its performance was validated using thermogravimetric analysis (TGA) and single-fiber tensile tests. The experimental program included tests on workability, compressive strength, flexural strength, splitting tensile strength, impact resistance, and high strain rate behavior using the reverse split Hopkinson pressure bar (RSHPB) method. Thermogravimetric analysis (TGA) and scanning electron microscope (SEM) confirmed that heat treatment removed surface sizing from carbon fibers (CF) with minimal effect on tensile strength. Replacing natural aggregates with MBOFS reduced slump but enhanced compressive, flexural, and splitting tensile strength. Incorporating 1% chopped CF further improved mechanical performance: 6 mm CF increased compressive strength, while 12 mm CF enhanced flexural and splitting tensile strength. Impact resistance improved with CF addition, with 12 mm CF slightly outperforming 6 mm. RSHPB tests showed higher dynamic strength for 6 mm CF specimens, with both strength and dynamic increase factor rising with strain rate and gas pressure.